Ti3AlC2

1. Chemical formula: Ti3AlC2

2. Constituent elements: Ti, Al, C

3. Molecular weight: 194.6

4. Chemical status: particles of micro and nano size

5. Appearance and character: dark brown particles with micro and nano size

1. Crystal structure: Hexagonal, P63/ MMC [194]

2. Cell parameters:

A =3.081 A, B =3.081 A, C =18.679 A;

α=90.00°, β= 90.00°, γ=120.00°;

3. PDF No.: JCPDS No. 52-0875 (refer to International Diffraction Data Center PDF-2004 database);

4. Density: 4.2 (g/cm3);

5 boiling point: ≥ 2700℃;

6. Melting point: ≥ 1300℃;

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder

The purity is above 98%, suitable for LiF+HCL method to etch and peel less (single) layer. Quantity gives great advantage.

Purity 99.99%, no impurities, suitable for any etching agent etching, a great amount of concessions.

The purity is 99%, and most of the articles published by foreign research groups use this material

Chemical Scientific Research Experiment Ti3AlC2 Black powder